結合相別性質表：
窒化物性質表
| TiN | ZrN | NbN | TaN | Cr2N | VN | |
|---|---|---|---|---|---|---|
| Nitrogen content[%] | 22.63 | 13.31 | 13.10 | 7.19 | 11.87 | 21.56 |
| Crystal structure | Cubic | Cubic | Hexagonal | Hexagonal | Hexagonal | Cubic |
| Lattice periods,kx. a | 4.249 | 4.537 | 2.959 | 2.933 | 4.806 | 4.136 |
| c | 11.271 | 2.864 | 4.479 | |||
| c/a | 3.804 | 0.98 | 0.928 | |||
| Density[g/cm3] calculated |
5.44 | 7.35 | 8.305 | 14.36 | 6.51 | 6.102 |
| experimental | 5.43 | 7.09 | 8.40 | 13.80 | 6.04 | |
| Microhardness 100g [kg/mm2] |
2050 | 1670 | 1461 | 1060 | 1571 | 1310 |
| Melting Point[℃] | 2950 | 2980 | 2300 | 3087 | 1650(分解） | 2050 |
| Heat of formation ΔH°(298）[Kcal/mol] |
-80.4 | -87.3 | -56.8±1.5 | -59.0 | -25.2 | -60.0 |
| Entropy S°(298) [Kcal/mol・℃] |
7.24±0.1 | 9.3±0.1 | 10.5±0.2 | 12.2±1.0 | 18.0±2.0 | 8.9±0.1 |
| Specific electrical resistance[μΩ・cm] at 20℃ |
40 | 18 | 54 | 198 | 84 | 60 |
| Point of transition to superconductivity °K |
5.6 | 9.8 | <1.94 | <4.2 | 8.2 |
（参考） データブック 高融点化合物便覧（モスクワ冶金出版所1976年版）
金属窒化物粉末は、耐食性、熱伝導性、電気伝導性が良好な製品群です。
これら粉末特性を活かし、導電材料用素材や硬質材料用素材として展開されております。
用途
TiNは、TiC基サーメット切削工具の特性改善に不可避の化合物であり、昨今のサーメットエ具の急速な伸びとともに需要が増大しています。またTiNは、粉末ハイス系合金の特性向上に役立っており、更に黄金色装飾合金としても使用されています。 TiN、ZrN、TaN等は、PVDコーティング用ターゲット材として、また酸化物系ならびに窒化物系セラミックスに導電性、熱伝導性を付加する添加材として用いられます。