結合相別性質表：
ホウ化物性質表
| TiB2 | ZrB2 | TaB2 | NbB2 | WB | MoB | CrB | LaB6 | |
|---|---|---|---|---|---|---|---|---|
| Boron content[%] | 31.11 | 19.16 | 10.67 | 18.88 | 5.55 | 10.13 | 17.21 | 31.83 |
| Crystal structure | Hexagonal | Hexagonal | Hexagonal | Hexagonal | Tetragonal | Tetragonal | Orthorhombic | Cubic |
| Lattice periods,kx. a | 3.026 | 3.168 | 3.078 | 3.089 | 3.115 | 3.110 | 2.969 | 4.1561 |
| b or c | 3.213 | 3.528 | 3.265 | 3.303 | 16.93 | 16.97 | b 7.858 C 3.002 | |
| c/a | 1.062 | 1.114 | 1.050 | 1.060 | 5.42 | 5.45 | ||
| Density[g/cm3] calculated |
4.530 | 6.09 | 12.62 | 7.00 | 15.734 | 8.665 | 6.11 | 4.722 |
| experimental | 4.38 | 6.17 | 12.38 | 6.97 | ～15.4 | 8.3 | 6.05 | 4.76 |
| Microhardness 30g [kg/mm2] |
3370±60 | 2252±22 | 2500±42 | 2600 | 3700(50g) | 2350(50g) | ～1300(100g) | 2770±60 |
| Melting Point[℃] | 2790 | 3200 | 3037 | 3000 | 2800 | 2550 | 2100 | 2530 |
| Heat of formation ΔH°(298）[Kcal/mol] |
-70.0 | -76.7 | -46 | -59 | -17 | -16.3 | (CrB2) -30 | -112.3 |
| Entropy S°(298) [Kcal/mol・℃] |
7.52 | 10.7 | 13.9 | 10.4 | 5.8 | |||
| Specific electrical resistance[μΩ・cm] at 20℃ |
9.0 | 9.7 | 32.5 | 25.7 | ～22 | 45 | 45.5 | 15.0 |
| Point of transition to superconductivity °K |
<1.28 | <1.80 | <1.28 | <1.0 | <1.28 | <1.28 | <1.28 | 5.7 |
（参考） データブック 高融点化合物便覧（モスクワ冶金出版所1976年版）
金属ホウ化物粉末は、機能性のある非常にユニークなニューセラミックス材料です。
高融点、高硬度且つ導電性、熱伝導性が良好で、放電加工による精密な仕上げが可能な耐熱・硬質材料として使用されております。
用途
TiB2は超硬質材としての需要が増大しており、また耐食材や蒸着用ボートにも用いられています。ZrB2は、融点、硬度、電気伝導度、熱伝導度が高い製品です。耐熱セラミックス、耐火材や超硬質材料として特性を発揮します。CrB,CrB2は他のホウ化物と比べて耐酸化性が良好であり、耐火材の長寿命化や、耐熱コーティングに適しています。MoBやWBは耐摩耗・耐食材として評価が高く、Fe、Ni系複ホウ化物サーメット材の主成分として重要です。LaB6は高い熱電子放射特性を持ち、種々の陰極材の用途開発に用いられます。また、単位重量あたりの近赤外線吸収に優れ、熱線遮蔽用途でも使用されます。